Carbon is one of the basic elements that has been used in electronics for a long time. Carbon occurs in various forms (allotropes) such as graphite, diamond, carbon nanotubes or graphene. In particular, carbon nanotubes and graphene are increasingly used in the field of electronic components and sensors. Carbon nanotubes can be modified by organic or inorganic substances and based on this to change their properties. Modified carbon nanotubes are preferably used as sensitive layers in environmental sensors. With the help of these materials, it is possible to realize simple planar sensors, where the appropriate type of modification gives the sensitivity to a certain analyte. The article presents different sensors for environmental parameters monitoring based on modified carbon nanotubes and graphene, including their measured basic electrical parameters and properties.
The paper was presented by Tomas Blecha from Department of Materials and Technology, Faculty of Electrical Engineering, University of West Bohemia, Pilsen, Czech Republic, at the 3rd PCNS 7-10th September 2021, Milano, Italy as paper No.1.4.
SENSORS FOR ENVIRONMENTAL PARAMETERS MONITORING
Carbon nanotubes (CNT) have a lot of unique properties. One of them is a large surface and the value of the property can reach 1000 m2/g. This is the reason why carbon nanotubes are good candidates for their use as an active layer in gas sensors development. Their enormous surface represents a lot of space for the interaction of gas molecules. Sensor properties are determined by a sensor active layer. The homogeneity of this layer is key to achieve the highest sensitivity and also affects the other properties of the sensor, therefore, the emphasis on deposition is very high.
Carbon nanotubes are very suitable material for sensitive layers of environmental parameters monitoring sensors such as dangerous gases, relative humidity and temperature. Defects in the CNT structure make it possible to modify with other materials and thus extend the detection capabilities to other analytes. The advantage of these modified CNTs is that chemoresistive sensors can be realized. It means the change of resistance or impedance of these sensors is due to analyte action. Thus, the evaluation electronics for these sensors can be very simple and the whole sensor system is suitable for integration into the Internet of Things system (IoT) because of low power consumption. If the carbon nanotubes are modified by suitable substances some parameters of these realized sensors can achieve better parameters such as sensitivity and selectivity.
Nitrogen dioxide (NO2) is characterized as a toxic gas that can damage human health at low concentrations. Electrochemical, resonance, optical and chemoresistive sensors are most commonly used to detect nitrogen dioxide gas. The active layer of these sensors is mostly made of metal oxides (SnO2, WO3, etc.). The disadvantage of these sensors is the need for heating at high temperatures (from 300 °C to 800 °C) to achieve the desired sensitivity and selectivity. Another disadvantage is using expensive deposition technologies such as vacuum deposition processes to create active layers of sensors. These disadvantages are partially removed by chemoresistive sensors with conductive polymer sensitive layers, but they are susceptible to environmental influences (humidity, UV radiation, etc.). The result is gradual degradation that leads to instability of the sensor. A possible solution can be found in composite materials, a combination of conductive polymers with other materials (e.g. Carbon NanoTubes – CNT). CNT, due to their properties, allows them to increase the long-term stability of the final active layer.
Eight different types of MWCNT modification by metal-phthalocyanines were tested and measured. The overview of all tested materials is shown in Figure 1. Sensors were tested in the hermetic man-made chamber under the 10 ppm NO2 concentration. This concentration corresponds to the highest permissible concentration in the working environment, also known as PEL (permissible exposure limit). The measurement conditions within the measuring chamber corresponded to the normal laboratory environment. The inside temperature was set to 22 °C, relative humidity 40 %, and gas flow rate 1 litre per minute. This setting simulates the common environment conditions where the sensors could potentially work.
The MWCNT-COOH PbPc(COONa)8 has a much better response to NO2 than pure carbon nanotubes. The sensor resistance dropped by more than 50 % of its absolute value during exposure to nitrogen dioxide. The response shows a very high sensitivity to this analyte (Fig. 3). The rapid resistance stabilization of the sensitive layer at the constant NO2 detection value is another feature improved by the modification and the partial spontaneous desorption of gas occurs. As a result of the desorption, the resistance almost always returns to the same value. This phenomenon eliminates the trend of resistance increase in the individual measurement cycles. Generally, this modification of the CNT leads to the improvement of all important features of the sensor.
references , , 
Ammonia is a colourless, very pungent and toxic gas. Ammonia is alkaline in nature, lighter than air and has a negative effect on human health, especially in higher concentrations, which, however, do not normally occur in the air. Inhalation of high concentrations, or even pure gases, leads to serious health problems (mucosal burns) and can even cause death. Commercially available sensors use the electrochemical principle. Using modified carbon nanotubes, it is possible to implement a chemoresistive ammonia sensor.
The carbon nanotubes from Brewer Science company were used for the creation of a thin sensitive layer on the interdigital electrodes by AJS. Before printing the water dispersion of these CNT contain 75 % single-wall carbon nanotubes (SWCNT) and 25 % multi-wall carbon nanotubes (MWCNT) was prepared. The surface of CNTs was covered by molecules of pyrene for better long-term stability. The carbon nanotubes were printed by the Aerosol Jet System on the flexible substrate. The deposited layer underwent optical inspection by scanning electron microscopy. In Figure 3 detail of carbon nanotubes net is shown. This Figure confirms the assumption that CNTs do not create any agglomeration when are printed by the Aerosol Jet System.
The sensors were exposed to ammonia and tested. The test was carried out at room temperature (21 °C) and relative humidity of 40 %. These conditions should simulate a common working environment of the sensor. Ammonia concentration was set at 50 ppm during the sensor testing. This level of concentration follows the maximum exposure limit that cannot be exceeded to avoid harm to human health.
The sensor showed high sensitivity to ammonia (Fig. 4). The resistance increases approximately by 25 % during the gas exposure at room temperature. The response of the sensor to ammonia is different from the response to nitrogen dioxide. The effect of ammonia increases the resistance of the sensitive layer based on CNTs, while the effect of nitrogen dioxide decreases the resistance.